Anycubic PETG Filament White 1 kg

Anycubic PETG Filament (White) 1 kg

Anycubic PETG filament combines the ease of printing characteristic of PLA with strength similar to ABS, offering durable and resilient models for everyday and more demanding applications. It stands out for its impact resistance of 45 kJ/m (X-Y), which allows prints to maintain their integrity even when dropped or subjected to stress. Additionally, the material is resistant to water, weather conditions, and many chemicals, making it well-suited for outdoor use.

Durability and Versatility

PETG retains its appearance and structure over time, without losing its gloss or properties when exposed to moisture or external factors. It is resistant to substances such as gasoline, detergents, perfumes, and toothpaste, which enhances its versatility. Thanks to these features, the material is suitable for the production of toys, enclosures, structural components, and mechanical prototypes.

Smart solutions and convenient use

The filament is equipped with an identification chip that works with the Anycubic ACE Pro, automatically recognizing print settings. The reusable spool with a threaded connection system reduces the risk of tangling and spilling, and its resistance to temperatures up to 80C increases durability. Before printing, the material should be dried and stored in a controlled humidity environment to avoid air bubbles and ensure a stable printing process.

Specifications

• Manufacturer: Anycubic
• Product code: IPHPEBW-102
• Color: White
• Weight: 1 kg
• Drying: Recommended
• Drying conditions: 55-65C, 8-10 h
• Compatibility with ACE Pro Multicolor Filament Box: Yes
• Recommended nozzle diameter: 0.2 mm or larger
• Nozzle temperature: 230-250C
• Build plate temperature: 60-70C
• Recommended print speed: 50-250 mm/s
• Maximum print volume: 12 mm/s
• Density: 1.23 g/cm³
• Material flow rate: 25-35 g/10 min
• Melting temperature: 130C
• Heat deflection temperature: 72C
• Deformation resistance: 69C
• Moisture absorption: 0.40
• Material stiffness: 1850-100 MPa
• Tensile strength: 52-1 MPa
• Elongation at break: 131
• Flexural stiffness: 2000-50 MPa
• Flexural strength: 80-2 MPa
• Impact resistance (X-Y): 45-2 kJ/m
• Tensile strength (Z-axis): 31-3 MPa