ANYCUBIC Water-Wash Resin 2.0 (transparent)

ANYCUBIC Water-Wash Resin 2.0 Transparent

ANYCUBIC Water-Wash Resin 2.0 is a photopolymer resin for LCD and DLP 3D printers. Its hydrophilic formula allows uncured resin residue to be washed away with water, simplifying post-processing without requiring isopropyl alcohol (IPA). The resin offers high print accuracy, increased crack resistance, reduced odour and protection against yellowing. With volumetric shrinkage of 2.2–5.5% and viscosity of 190–230 mPa·s, it produces detailed prints with smooth surfaces and good durability.

Water-based cleaning

Resin residue can be removed using water alone, without IPA. This simplifies the cleaning of finished models and can reduce operating costs while maintaining print quality.

Crack resistance and durability

With an elongation at break of 16–22%, the cured resin provides mechanical strength and increased resistance to cracking. It is suitable for parts that need to retain stiffness and resist deformation.

Print accuracy and resistance to yellowing

Low volumetric shrinkage supports detailed models and accurate printing. The resin enables a stated precision of 0.15 mm, helping reproduce fine details. Its improved formula also reduces the risk of yellowing, helping models retain their appearance over time.

Stable printing and compatibility

The resin maintains low viscosity at temperatures of 15–20°C, supporting smooth material flow and stable printing. Improved build-plate adhesion helps reduce the risk of print failure. It is compatible with LCD and DLP printers using UV curing technology at 405 nm, for home or professional use.

Specifications

• Manufacturer: ANYCUBIC
• Model: Water-Wash Resin 2.0
• Colour: Transparent
• Material: Light-curable resin modified with hydrophilic groups
• Wavelength: 365–405 nm
• Viscosity: 190–230 mPa·s at 25°C
• Density: 1.07–1.09 g/cm³
• Hardness: 82–85 HD
• Tensile strength: 38–43 MPa
• Elongation at break: 16–22%
• Flexural modulus: 48–60 MPa
• Flexural strength: 2300–3000 MPa
• Young’s modulus: 1100–1300 MPa
• Izod impact strength: 133 J/m
• Volumetric shrinkage: 2.2–5.5%
• Printing temperature: 20–50°C
• Recommended ambient temperature during printing: 20–40°C
• First-layer exposure time: 25–40 s
• Standard-layer exposure time: 2–2.5 s
• Cleaning agent: 95% IPA or water
• Cleaning time: At least 3 min with 95% IPA; at least 5 min with water (medium)
• UV wavelength during curing: 405 nm
• Curing temperature: 18–30°C
• UV irradiance: 25,000–30,000 µW/cm²
• Curing time: 3 min
• Weight: 1 kg