ANYCUBIC Water-Wash Resin 2.0 (gray)

ANYCUBIC Water-Wash Resin 2.0 Gray

ANYCUBIC Water-Wash Resin 2.0 is a photopolymer resin for LCD and DLP 3D printers. Its hydrophilic formula allows uncured resin residue to be removed with water, without requiring isopropyl alcohol (IPA). This simplifies post-processing and can reduce cleaning costs. The resin also offers high print accuracy, increased crack resistance, reduced odour and anti-yellowing properties. With volumetric shrinkage of 2.2–5.5% and viscosity of 190–230 mPa·s, it produces detailed prints with smooth surfaces and good durability.

Water-based cleaning

Resin residue can be removed using water alone, without IPA. This makes cleaning finished models more convenient while maintaining print quality. The specified cleaning time in water is at least 5 minutes.

Crack resistance and durability

The resin has an elongation at break of 16–22%. Once cured, models offer increased mechanical strength and resistance to cracking. The material is suitable for applications where finished parts need to retain stiffness and resist deformation.

Print accuracy and resistance to yellowing

Low volumetric shrinkage supports detailed models and accurate prints. The stated precision is 0.15 mm, helping reproduce fine details. The improved formula also reduces the risk of yellowing, helping models retain their appearance over time.

Stable printing and compatibility

The resin maintains low viscosity at temperatures of 15–20°C, supporting smooth material flow and stable printing. Improved build-plate adhesion helps reduce the risk of print failure. It is compatible with LCD and DLP printers using UV curing technology at 405 nm, for home and professional use.

Specifications

• Manufacturer: ANYCUBIC
• Model: Water-Wash Resin 2.0
• Colour: Gray
• Material: Light-curable resin modified with hydrophilic groups
• Wavelength: 365–405 nm
• Viscosity: 190–230 mPa·s at 25°C
• Density: 1.07–1.09 g/cm³
• Hardness: 82–85 HD
• Tensile strength: 38–43 MPa
• Elongation at break: 16–22%
• Flexural modulus: 48–60 MPa
• Flexural strength: 2300–3000 MPa
• Young’s modulus: 1100–1300 MPa
• Izod impact strength: 133 J/m
• Volumetric shrinkage: 2.2–5.5%
• Printing temperature: 20–50°C
• Recommended ambient temperature during printing: 20–40°C
• First-layer exposure time: 25–40 s
• Standard-layer exposure time: 2–2.5 s
• Cleaning agent: 95% IPA or water
• Cleaning time: At least 3 min with 95% IPA; at least 5 min with water
• UV wavelength during curing: 405 nm
• Curing temperature: 18–30°C
• UV irradiance: 25,000–30,000 µW/cm²
• Curing time: 3 min
• Weight: 1 kg