ANYCUBIC Water-Wash Resin 2.0 (gray)

ANYCUBIC Water-Wash Resin 2.0 Gray

ANYCUBIC Water-Wash Resin 2.0 is a photopolymer resin for LCD and DLP 3D printers. Its hydrophilic formula allows uncured resin residue to be washed away with water, without requiring isopropyl alcohol (IPA). This simplifies post-processing and can reduce cleaning costs. The resin is designed to deliver accurate prints, improved crack resistance, reduced odour and resistance to yellowing. Its volumetric shrinkage of 2.2–5.5% and viscosity of 190–230 mPa·s support detailed prints with smooth surfaces.

Water-based cleaning

Resin residue can be removed using water alone, without IPA. This makes cleaning finished models more convenient while maintaining print quality. The listed cleaning options also include 95% IPA.

Crack resistance and durability

With an elongation at break of 16–22%, the cured resin offers increased mechanical strength and resistance to cracking. It is suitable for parts where stiffness and low susceptibility to deformation are important.

Print accuracy and resistance to yellowing

Low volumetric shrinkage helps produce detailed models with high dimensional accuracy. The stated precision is 0.15 mm, supporting faithful reproduction of small details. The improved formula also helps reduce yellowing and preserve the appearance of printed models.

Stable printing and compatibility

The resin is compatible with LCD and DLP printers using UV curing technology in the 365–405 nm wavelength range, including 405 nm systems. Its low viscosity supports material flow and stable printing, while improved build-plate adhesion helps reduce the risk of print failure. The stated printing temperature is 20–50°C, with a recommended ambient temperature of 20–40°C.

Specifications

• Manufacturer: ANYCUBIC
• Model: Water-Wash Resin 2.0
• Colour: Gray
• Material: Light-curable resin modified with hydrophilic groups
• Wavelength: 365–405 nm
• Viscosity: 190–230 mPa·s at 25°C
• Density: 1.07–1.09 g/cm³
• Hardness: 82–85 HD
• Tensile strength: 38–43 MPa
• Elongation at break: 16–22%
• Flexural modulus: 48–60 MPa
• Flexural strength: 2300–3000 MPa
• Young’s modulus: 1100–1300 MPa
• Izod impact strength: 133 J/m
• Volumetric shrinkage: 2.2–5.5%
• Printing temperature: 20–50°C
• Recommended ambient temperature during printing: 20–40°C
• First-layer exposure time: 25–40 s
• Standard-layer exposure time: 2–2.5 s
• Cleaning agent: 95% IPA or water
• Cleaning time: 95% IPA: ≥3 min; water: medium, ≥5 min
• UV wavelength during curing: 405 nm
• Curing temperature: 18–30°C
• UV irradiance: 25,000–30,000 µW/cm²
• Curing time: 3 min
• Weight: 1 kg