ANYCUBIC ABS-Like Resin 3.0 (Gray)

ANYCUBIC ABS-Like Resin 3.0 is a gray photopolymer resin for LCD and DLP 3D printers. It combines high mechanical strength, crack resistance and print accuracy. With an elongation at break of 25–30%, an Izod impact strength of 130 J/m and volumetric shrinkage of 3.9–4.9%, it produces durable models with smooth surfaces and fine detail. Its low viscosity and reduced odour support comfortable use.

Flexibility and strength

ABS-Like Resin 3.0 is suitable for parts exposed to mechanical stress. Its hardness of 83–86 HD and high impact resistance help printed models retain their durability during drilling and further machining. Low susceptibility to warping makes the resin suitable for mechanical parts, device housings and automotive components. With elongation at break of up to 30%—nearly twice that of many standard ABS-type resins—the material can better withstand stress and resist damage during everyday use.

Print accuracy and speed

Low shrinkage and a viscosity of 280–300 mPa·s support accurate detail reproduction and a smooth surface finish. Good flow helps the resin return to the build area quickly, reducing print times and supporting higher productivity.

Compatibility and printing comfort

The resin is formulated to minimise odour and reduce the risk of irritation during use. It is compatible with a wide range of LCD and DLP 3D printers using UV light with a wavelength of 365–405 nm, making it suitable for home workshops and more advanced projects.

Specifications

• Manufacturer: ANYCUBIC
• Model: ABS-Like 3.0
• Colour: Gray
• Material: Photopolymer resin
• Wavelength: 365–405 nm
• Viscosity: 280–300 mPa·s at 25°C
• Density: 1.06–1.09 g/cm³
• Hardness: 83–86 HD
• Tensile strength: 38–45 MPa
• Elongation at break: 25–30%
• Flexural modulus: 50–65 MPa
• Flexural strength: 1500–2000 MPa
• Young’s modulus: 1300–1700 MPa
• Izod impact strength: 130 J/m
• Volumetric shrinkage: 3.9–4.9%
• Printing temperature: 20–50°C
• Recommended ambient temperature during printing: 20–40°C
• First-layer exposure time: 23–40 s
• Standard-layer exposure time: 2–3.6 s
• Cleaning agent: 95% IPA
• Washing time: ≥3 min
• UV wavelength during curing: 405 nm
• Curing temperature: 18–30°C
• UV irradiance: 25,000–30,000 µW/cm²
• Curing time: 3 min
• Weight: 1 kg