ANYCUBIC ABS-Like Resin 3.0 (Black)

ANYCUBIC ABS-Like Resin 3.0

ANYCUBIC ABS-Like Resin 3.0 is a black photopolymer resin for LCD and DLP 3D printers. It combines high mechanical strength, crack resistance and print accuracy. With an elongation at break of 25–30%, an impact strength of 130 J/m and low volumetric shrinkage of 3.9–4.9%, it produces durable models with smooth surfaces and fine detail. Its low viscosity and reduced odour also support comfortable handling.

Flexibility and strength

ABS-Like Resin 3.0 is suitable for parts exposed to mechanical stress. Its hardness of 83–86 HD and high impact resistance help printed models withstand drilling and further machining. Low warping makes it suitable for mechanical parts, device enclosures and automotive components. With elongation at break of up to 30%—nearly twice that of many standard ABS-type resins—the material can better withstand stress and resist damage during everyday use.

Precision and print speed

Low shrinkage and a viscosity of 280–300 mPa·s support accurate detail reproduction and a smooth surface finish. Good flow helps the resin return to the build area quickly, reducing print times and improving productivity.

Printer compatibility and working conditions

The resin is compatible with a wide range of LCD and DLP 3D printers using UV light with a wavelength of 365–405 nm. Its formula is designed to minimise odour and reduce the risk of irritation during use.

Specifications

• Manufacturer: ANYCUBIC
• Model: ABS-Like 3.0
• Colour: Black
• Material: Photopolymer resin
• Wavelength: 365–405 nm
• Viscosity: 280–300 mPa·s at 25°C
• Density: 1.06–1.09 g/cm³
• Hardness: 83–86 HD
• Tensile strength: 38–45 MPa
• Elongation at break: 25–30%
• Flexural modulus: 50–65 MPa
• Flexural strength: 1500–2000 MPa
• Young’s modulus: 1300–1700 MPa
• Izod impact strength: 130 J/m
• Volumetric shrinkage: 3.9–4.9%
• Printing temperature: 20–50°C
• Recommended ambient temperature during printing: 20–40°C
• First-layer exposure time: 23–40 s
• Standard-layer exposure time: 2–3.6 s
• Cleaning agent: 95% IPA
• Washing time: ≥3 min
• UV wavelength during curing: 405 nm
• Curing temperature: 18–30°C
• UV irradiance: 25,000–30,000 µW/cm²
• Curing time: 3 min
• Weight: 1 kg