ANYCUBIC Tough Resin Ultra (white)

ANYCUBIC Tough Resin Ultra (White)

ANYCUBIC Tough Resin Ultra is a photopolymer resin for LCD and DLP 3D printers. Its key features are high flexibility and resistance to mechanical damage. With an elongation at break of 70–80%, printed models retain their strength, are less prone to cracking and quickly return to their original shape after deformation. The resin is designed for durable functional models, moving parts and prints exposed to impacts, bending or long-term use. Its specially formulated composition also reduces odour during printing.

Flexibility and crack resistance

The resin combines elasticity and impact resistance with the ability to maintain structural integrity, including in thin-walled parts. It resists cracking under stress and quickly returns to its original shape after deformation, helping finished models withstand accidental drops, transport and intensive use.

Fine detail and versatile applications

ANYCUBIC Tough Resin Ultra reproduces fine details such as hair, textures and small structural features. It is also suitable for models with moving parts, allowing individual components to be adjusted or replaced.

Durability and resistance to external factors

The material is formulated to reduce the effects of moisture and UV radiation on finished prints. It offers resistance to brittleness, corrosion and deformation, including during long-term storage. Low moisture absorption helps models maintain dimensional stability over time.

Use on its own or mixed with other resins

ANYCUBIC Tough Resin Ultra can be used as a primary printing material or as an additive to other resins. Mixing it with other materials increases the impact resistance and durability of finished models.

Printer compatibility

Optimised for Anycubic LCD printers, the resin is also compatible with other LCD and DLP printers that use UV light with a wavelength of 405 nm.

Specifications

• Manufacturer: ANYCUBIC
• Model: Tough Resin Ultra
• Colour: White
• Material: Photopolymer resin
• Wavelength: 365–405 nm
• Viscosity: 500–900 mPa·s at 25°C
• Density: 1.05–1.25 g/cm³
• Hardness: 71–75 HD
• Tensile strength: 20–28 MPa
• Elongation at break: 70–80%
• Flexural modulus: 15–25 MPa
• Flexural strength: 350–800 MPa
• Young’s modulus: 350–450 MPa
• Volumetric shrinkage: 5.1–6.2%
• Printing temperature: 20–50°C
• Recommended ambient temperature during printing: 20–40°C
• First-layer exposure time: 20–40 s
• Standard-layer exposure time: 1.5–3 s
• Cleaning agent: 95% IPA
• Cleaning time: ≥3 min
• UV wavelength during curing: 405 nm
• Curing temperature: 18–30°C
• UV irradiance: 25,000–30,000 µW/cm²
• Curing time: 3 min
• Weight: 1 kg