ANYCUBIC ABS-Like Resin Pro 2 (Gray)

ANYCUBIC ABS-Like Resin Pro 2 (Gray)

ANYCUBIC ABS-Like Resin Pro 2 is a photopolymer resin developed for applications requiring high mechanical strength and excellent damage resistance. Its elongation at break of 35–40% provides greater flexibility and helps reduce cracking. With volumetric shrinkage of 4.3–5.6%, a viscosity of 300–400 mPa·s and impact strength of up to 212 J/m, it produces durable, highly detailed models.

Strength and resistance to deformation

ABS-Like Resin Pro 2 combines high tensile and flexural strength with flexibility, with elongation at break reaching 35–40%. It is suitable for printing structural components, handles, assembly jigs and industrial prototypes.

Precision and printing efficiency

The resin’s low viscosity and good flow help reduce the time required to cure successive layers and support an efficient model-forming process. Good build-plate adhesion helps minimise the risk of failed prints. Low shrinkage helps preserve detail accuracy and produce smooth model surfaces.

Reduced odour

The specially developed formula reduces odour during printing, making the resin more comfortable to use, particularly during extended printing sessions.

Printer compatibility

This resin is compatible with LCD and DLP printers using UV light with a wavelength of 365–405 nm. It is optimised for ANYCUBIC LCD printers and can also be used with other compatible devices.

Specifications

• Manufacturer: ANYCUBIC
• Model: ABS-Like Resin Pro 2
• Colour: Gray
• Material: Photopolymer resin
• Wavelength: 365–405 nm
• Viscosity: 300–400 mPa·s at 25°C
• Density: 1.05–1.25 g/cm³
• Hardness: 82–84 HD
• Tensile strength: 35–45 MPa
• Elongation at break: 35–40%
• Flexural modulus: 40–45 MPa
• Flexural strength: 1,400–1,800 MPa
• Young’s modulus: 1,600–1,800 MPa
• Izod impact strength: 212 J/m
• Volumetric shrinkage: 4.3–5.6%
• Printing temperature: 20–50°C
• Recommended ambient temperature during printing: 20–40°C
• First-layer exposure time: 20–40 s
• Standard-layer exposure time: 1.5–3 s
• Cleaning agent: 95% IPA
• Washing time: ≥3 min
• UV wavelength during curing: 405 nm
• Curing temperature: 18–30°C
• UV irradiance: 25,000–30,000 µW/cm²
• Curing time: 3 min
• Weight: 1 kg