ANYCUBIC IPHTFBK-101 PETG-CF Filament 1 kg black

ANYCUBIC IPHTFBK-101 PETG-CF Filament 1 kg (Black)

ANYCUBIC PETG-CF IPHTFBK-101 is a carbon fiber-reinforced filament that offers significantly better stiffness and impact resistance compared to standard PETG. Thanks to its reinforced structure, prints are more resistant to pressure and mechanical damage, making it ideal for demanding applications. Parameters such as an Izod impact strength of 60 kJ/m, an impact resistance of 3100 MPa, and a material stiffness of 2550 MPa confirm the material's increased durability.

Aesthetics and durability in all conditions

The addition of carbon fiber gives prints a satin-matte surface while masking layer lines, improving the appearance of models without additional post-processing. The filament is distinguished by high resistance to water and weather conditions, allowing it to retain its color and structure even with long-term outdoor use. The material's low shrinkage and high resistance to deformation translate into dimensional stability and high print quality, particularly in precision parts.

Easy printing and practical solutions

The material is easy to use and compatible with desktop printers, ensuring a smooth printing process and minimal risk of clogging (a hardened steel nozzle is recommended). A built-in chip enables automatic filament identification in the Anycubic ACE Pro system, simplifying setup. A reusable spool with a threaded system enhances stability and reduces the risk of tangling, while heat resistance up to 100°C and compatibility with most spool-free filaments improve user convenience.

Specifications

• Manufacturer: Anycubic
• Model: IPHTFBK-101
• Color: black
• Weight: 1 kg
• Compatibility with ACE Pro Multicolor Filament Box: yes
• Recommended nozzle diameter: 0.4 mm
• Nozzle temperature: 240-270°C
• Bed temperature: 65-75°C
• Recommended print speed: 40-250 mm/s
• Cooling time: 6 s
• Maximum flow rate: 11 mm/s
• Density: 1.32 g/cm³
• Material flow rate: 14.1 ± 1.6 g/10 min (190°C / 2.16 kg)
• Melting temperature: 221°C
• Vicat softening temperature: 74°C
• Heat deflection temperature (0.45 MPa): 67°C
• Water absorption: 0.38
• Material stiffness (Young's modulus): 2550 ± 100 MPa
• Tensile strength: 54 ± 2 MPa
• Elongation at break: 12 ± 1
• Impact strength (Izod): 3100 ± 150 MPa
• Flexural strength: 88 ± 2 MPa
• Izod impact strength (X-Y): 60 ± 4 kJ/m
• Tensile strength (Z): 37 ± 3 MPa